STARBLAZE 32F08 CHEMICAL RESISTANT PU (C5) COATING
Description:
Starblaze 32F08 is a two component, Nano additive based PolyUrethane resin cured with an aliphatic isocyanate based curative. The presence of Nano additives enhances the barrier performance of the coating solution against the water, UV rays, chemical fumes & corrosive environment of C5 class thus leading to extension of the life of the coating. The Nano additives makes provides an impermeable top layer that repel moisture and stops the penetration through top coat film resulting in high durability of the protective shield.
Application Areas
- Refineries
- Metal Bridges & Tanks
- Marine & Offshore cooling towers /platforms.
- Structural Steel
- Pulp and paper mills
- Pipelines.
- Chemical processing plants
| Product Name | STARBLAZE 32F08 CHEMICAL RESISTANT PU (C5) COATING |
|---|---|
| Type | Polyester-Urethane |
| Density | 1.20±0.05 kg /ltr |
| Mixing ratio(L:H) | 2:1 (by Volume) |
| Solids content | 60±3% |
| Coverage(theoretical) | 13.00 sq mtr /ltr @40 |
| DFT /1 Coats (Practical- brush application 8.5 sq mtr /ltr-singe coat) | - |
| Humidity resistance (ASTM-D4585) | 2000Hrs |
| Adhesion (ASTM D4541) | >1000psi |
| Temperature resistance | Upto 90°C |
| Adhesion on Primer & Undercoat | Excellent |
| Corrosion resistance (ASTM B117)(with system) | >2000 Hrs |
| Corrosion Weathering (ASTM D5984) (with system) | >3000 Hrs |
| Abrasion resistance, Wt. loss (1000cycle-1kg) | <5mg |
| QUV(Weather resistance) Excellent | (>1100 hours) |
| Drying time (set to touch) | 20-30 min@ 1.5mil dry |
| Film | - |
| Recoating | 2 to 4 hours after touch |
| Dry | - |
| Functional cure | 8-12 Hrs |
| Full cure | 72 hrs |
Excellent.